P7100CF
Carbon-filled PA12
← Back to material selection
MATERIAL OVERVIEW
Properties to guide your selection.
A PA12-based SLS material reinforced with carbon fibre. It is intended for components needing more strength and rigidity than an unfilled nylon option, with thermal performance also considered.
Selection considerations
Confirm the fibre content and grade-specific properties.
Discuss this material →| Printing process | SLS |
|---|---|
| Supplier-listed dimensional accuracy | ±0.2mm |
| Listed colours | Dark grey |
| Tensile strength | 55MPa |
| Tensile modulus | 4000MPa |
| Elongation at break | 10% |
| Flexural strength | 52MPa |
| Flexural modulus | 5000MPa |
| Heat deflection temperature | 155°C |
Heat deflection temperature is a test result, not a continuous-use temperature. Dimensional requirements are reviewed against the drawing.